Product Families

PolyWood™

This Specialty family provides unique filaments from Polymaker to unlock new 3D printing applications.

PolyWood™ is a wood mimic filament without actual wood powder, which removes all risks of nozzle clogs. PolyWood™ is made entirely with PLA using a special foaming technology. It exhibits the same density and appearance as wood.

  • Specialty
  • Wood
  • 1.75 mm
  • 2.85 mm
  • 600g
FIND A RESELLER
SKU: N/A Category:

Description

PRINT SETTINGS

Nozzle Temperature:
190˚C – 210˚C

Printing Speed:
35mm/s – 50mm/s

Bed Temperature:
25˚C – 60˚C

Bed Surface:
Glass with glue, blue tape, BuilTak®

Cooling Fan:
ON

MECHANICAL PROPERTIES

Young’s Modulus:
N/A

Tensile Strength:
23.2 ± 0.4 Mpa

Bending Strength:
52.9 ± 0.3 Mpa

Impact Strength:
2.1 ± 0.2 kJ/m2

THERMAL PROPERTIES

Glass Transition Temperature:
62˚C

Vicat Softening Temperature:
60˚C

Melting Temperature:
151˚C

NOTES

Drying Settings:
70˚C for 8h

Recommended Support Materials:
PolyDissolve™ S1

Other:
N/A

TDS:
Download

SDS:
Download

TECHNOLOGY

PolyWood™ features Polymaker's Jam-Free™ technology and Polymaker's Stabilized Foaming™ technology:

Jam-Free™ technology improves the heat stability of Polymaker’s PLA filaments with softening temperatures over 140 °C. As a result, Polymaker’s PLA filaments show minimal softening in the “cold end” and can melt rapidly once entering the heating zone, leading to excellent printing quality with zero risk of nozzle jams.


Stabilized Foaming™ technology is used to produce foamed filaments, whose foam structure can survive the printing process and be inherited by the printed parts. This enables light weight 3D printed parts with unprecedented surface finish.