View our material charts to find the suitable filament for your application.
For more detailed technical data visit our webapp：Full Technical Data Comparison

Dry state

Wet state

Printability

The printability of the material is defined by its ease of use and equipment required.

Rigidity

The rigidity of the material is defined by its modulus:Young’s modulus
ISO 527, GB/T 1040.

Heat Resistance

The heat resistance of the material is defined by its VST: Vicat Softening temperature
ISO 306 GB/T 1633.

Weather Resistance

The weather resistance of the material is defined by its UV resistance. The data provided is currently an estimation.

Durability

The durability of the material is defined by its resistance to impact:Charpy impact strength
ISO 179, GB/T 1043.A

*PolyMide™ PA6-CF and PolyMide™ PA6-GF heat resistance are defined by their HDT: Heat Deflection Temperature
ISO 75 0.45 MPa.

PolyLite™ Series

PolyLite™ PLA Pro

PolyLite™ PLA Pro is a first of its kind, combining high toughness and high rigidity, this professional PLA offers engineering properties without compromising the ease of printing of regular PLA. PLA PRO is the perfect candidate for a wide range of applications covering functional prototyping, jigs and fixtures and end use parts for consumer goods.

High impact strength

Easy to use

Excellent printability

Find a Reseller

Color Range

Regular

Metallic

Inquiry

Product Availability

Product Information Sheet

Safety Data Sheet

Technical Data Sheet

FAQ

What is Jam-Free Technology?

Polymaker Jam-Free Technology increases the heat resistance of the filament itself (not the printed part) to 140°C.
This prevent any jamming issue due to the hot end heat creep issue.
Heat creep is the process of heat spreading irregularly throughout your hot end, softening the filament before entering the melting chamber and jamming the filament by making it expand in the cold end..
The increase of the filament heat resistance from 60°C to 140°C ensures a Jam-Free experience.
(Note the printed part will have the same heat resistance as regular PLA: ~60°C)

What is the difference between PolyLite™ PLA, PolyMax™ PLA and PolyLite™ PLA Pro?

PolyLite™ PLA is a very rigid material with very low impact resistance.
PolyMax™ PLA is an extremely ductile material with high impact resistance and durability.
PolyLite™ PLA Pro is the best of both worlds combining excellent rigidity and high impact strength.

Are there any metallic particles in PLA Pro Metallic series?

No, the PolyLite™ PLA Pro Metallic series does not contain actual metal particles in the material.

What is the difference between PolyLite™ PLA, PolyMax™ PLA and PolyLite™ PLA Pro?

Are there any metallic particles in PLA Pro Metallic series?

No, the PolyLite PLA Pro Metallic series does not contain actual metal particles in the material.

1.0 kg

3.0 kg

5.0 kg

Specifications

PolyLite™ PLA Pro

print
settings

Printing Temperature:

190˚C - 220˚C

Bed Temperature:

30˚C - 60˚C

Printing Speed:

30mm/s -70mm/s

Fan:

Direct Drive Retraction Distance:

3mm

Direct Drive Retraction Speed:

60mm/s

Indirect Drive Retraction Distance:

1mm

Indirect Drive Retraction Speed:

30mm

Recommended Support Materials:

PolyDissolve™ S1/PolySupport™

Dry Settings:

55˚C for 6h

(Only if the material has absorbed moisture)

MEchanical Properties

(XY)Young's Modulus (MPa):

2932.2 ± 55.3 MPa

ISO 527, GB/T 1040

(Z)Young's Modulus (MPa):

2633.0 ± 117.4 MPa

ISO 527, GB/T 1040

(XY)Tensile Strength:

49.8 ± 0.4 MPa

ISO 527, GB/T 1040

(Z)Tensile Strength:

36.5 ±0.6 MPa

ISO 527, GB/T 1040

(XY)Elongation at break(%):

6.3 ± 0.9 %

ISO 527, GB/T 1040

(Z)Elongation at break(%)

2.4 ± 0.3 %

ISO 527, GB/T 1040

(XY)Bending Modulus (MPa):

2933.8 ± 78.3 MPa

ISO 178, GB/T 9341

(XY)Bending Strength (MPa):

77.9 ± 0.4 MPa

ISO 178, GB/T 9341

(XY)Charpy Impact Strength:

17.1 ±1.2 kJ/m2

ISO 179, GB/T 1043

Thermal Properties

Glass Transition Temperature:

62.0 °C

DSC, 10°C/min

Melting Temperature:

62.0 °C

DSC, 10°C/min

Heat Deflection Temperature
(1.8MPa):

57.6 °C

ISO 75 1.8MPa

Heat Deflection Temperature
(0.45MPa)

59.3 °C

ISO 75 0.45MPa

Vicat Softening Temperature:

62.7 °C

ISO 306, GB/T 1633

Material Properties

Technology

Jam-Free™ technology improves the heat stability of Polymaker’s PLA filaments with softening temperatures over 140 °C. As a result, Polymaker’s PLA filaments show minimal softening in the “cold end” and can melt rapidly once entering the heating zone, leading to excellent printing quality with zero risk of nozzle jams.

PolyLite™ PLA Pro